SELLAN MORTERO

MORTERO EPOXI, REPAIR OF CRACKS IN INDUSTRIAL SOILS

PROPERTIES  :
To make epoxy mortars in:
– Expansion joint lips.
– Machinery benches.
– Concrete adhesives.
– Increased pavements.
– Repairs.
– Coke filling.

SELLAN MORTERO PREPARATION :
– 1 Part of the catalyzed base.
– 7-8 Quartz parts, (granulometry between dust and 1.2 mm. With linear particle distributions, that is, that there are all sizes so that there are no gaps). This dough is perfectly homogenized, either with vertical blade homogenizer or manually.
Note: ANCHOR LAYER, before adding the quartz, mix the base and the catalyst and with a brush spread over the entire surface where we are going to spread the Mortar Seal a small layer as a primer.
– Pouring of the SELLAN MORTERO onto the anchor layer while still sticky, that is, from 15 minutes applied to 1-1 / 2 H.
– Extended with ruler on tracks of 4 – 6 mm.
– Smoothing and correction of imperfections with the help of a trowel. In case of having to endure strong chemical attacks, a last layer of SELLAN RESIN can be applied on the floor.

PROPERTIES :
Sellan Mortar is a preparation based on epoxy resins and quartz filler. The structure formed once set has extraordinary adhesion and high resistance to abrasion, also resists extreme temperatures and excellent resistance to chemical agents.

PAVEMENT CAN BE USED :
For pedestrian traffic At => 24 hours
For the traffic of elem. light at => 2 days
For truck traffic After => 5 days
Total hardening At => 7 days

CHEMICAL RESISTORS IN IMMERSION :
Sulfuric acid => 20% => 300 hours => Unaltered
Sulfuric acid => 50% => 300 hours => Decolora
Phosphoric acid => 90% => 300 hours => Unaltered
Acetic acid => 5% => 300 hours => Whiten
Nitric acid => 20% => 300 hours => Decolor
Oleic acid => 100% => 300 hours => Unaltered
Citric acid => 100% => 300 hours => Unaltered
Caustic soda => 50% => 300 hours => Unaltered
Xylene => 100% => 300 hours => Unaltered
Oil => 100% => 300 hours => Unaltered
Gasoline => 100% => 300 hours => Unaltered
Sugary solution => 20% => 300 hours => Unaltered
Aviation fuel => 100% => 300 hours => Unaltered

MECHANICAL RESISTORS :
Compression : 1800 Kg / cm2 => ASTM C-306-55
Flexion : 480 Kg / cm2 => ASTM C-293-57 T
Traction : 100 Kg / cm2 => ASTM C-190-58

SAFETY ADVISES :
H315 Causes skin irritation. H317 May cause an allergic skin reaction. H319 Causes serious eye irritation. H411 Toxic to aquatic organisms, with lasting harmful effects. P273 Avoid release to the environment. P280 Wear gloves / clothing / glasses / protective mask. P501 Dispose of contents / container at an authorized treatment point. P302 + P352 IF IN SKIN: Wash with plenty of water / … P332 + P313 In case of skin irritation: Consult a doctor. P337 + P313 If eye irritation persists: Consult a doctor. P305 + P351 + P338 IF IN EYES: Rinse cautiously with water for several minutes. Remove contact lenses, if worn and easy. Continue rinsing. Contains: reaction product: bisphenol-A-epichlorohydrin, epoxy resins (mean molecular weight <= 700) oxirane, mono [(C12-14-alkyloxy) methyl] derivatives Triisobutyl phosphate.

Type of packaging  :
SELLAN MORTERO is supplied in a 10 Kg KIT.
It contains each KIT :
* Base component : 1,334 Kg.
* Catalyst component : 0.666 Kg.
* Quartz component : 8.0 Kg.

RECORDS  :
Nº article: 101985
Industrial Register: 154069
Review / Data: 15 / March / 2016

PHYSICAL PROPERTIES :
Nature : Solventless epoxy resin
Color : Colorless
Special weight At 21ºC : 1.9 gr / cc (mixed the 3 components)
Mixing ratio : 7 parts component base, 3 parts component catalyst
Mixing shelf life : 30 minutes at 20ºC
Yield approx : 2 m2 / Kg.

QUALITATIVE COMPOSITION :
Epoxy resins
Charge (Quartz)

 

WARNINGS:
The suggestions and recommendations on the use of our products meet our most knowledge at the time of writing this data sheet. We are not responsible for any possible negligence in handling. Compliance with all laws, including those in the protection of industrial property rests solely with the users of our products.